剛玉磨料YF2A
分類: 剛玉磨料YF2A  發布時間: 2013-12-12 22:51 

剛玉磨料YF2A

剛玉磨料YF2A系列產品

Corundum Abrasive YF2A Series Products


鄭州玉發磨料有限公司生產的剛玉磨料YF2A是以工業氧化鋁為主要原料,配加適量的復合添加劑,經高溫熔煉而成。該產品既具有白剛玉磨料的鋒利,又具備棕剛玉、鉻剛玉磨料的韌性。用于樹脂砂輪、涂覆磨具的制備,性能可與藍色剛玉和藍單媲美。適用于特種鋼的切割和磨削,特別是用于干磨和易變形易燒傷工件的磨削加工可采用各種結合劑

The corundum abrasives YF2A series products of Zhengzhou Yufa Abrasive Co., Ltd. are produced using industrial alumina as the main raw material, adding composite additives, and melting at high temperatures. The products possess properties of both good sharpness equal to white corundum and high toughness to brown corundum or chrome corundum . They can be used as raw material when making resin abrasive disks and coated milling tools, and the properties of the products are completely comparable to the blue corundum and blue monocrystal corundum. The products can be used for cutting and grinding special steel ,especially for dry-grinding and making workpieces which are easy-out-of-shape and easy getting burnt. All kinds of binders can be adopted when utilizing YF2A to make grinding tools.

 

鄭州玉發磨料有限公司生產的剛玉磨料YF2A系列產品呈淺黃色(如圖),各項理化指標如下:

 

The color of the YF2A series corundum abrasives produced by Yufa is light yellow  (see the image below). The product indice are as follows:

 

化學成份 Chemical composition:

            Al2O3 99%    Na2O0.40%  

SiO20.20%    Fe2O30.10%

粒度組成: 符合GB2477-2008標準

Particle size :  in accordance of the specifications of GB2477-2008.

 

典型試驗:Typical test

  切割試驗 cutting test

1)采用該產品、整形棕剛玉、磨棕剛玉、對輥棕剛玉分別制備成

φ105*1mm切割片,在切割304不銹鋼φ12棒材試驗,結果如下。

Use YF2A, shaped brown corundum, ball-milled brown corundum and roller- milled brown corundum respectively to make Cutting disks in size of φ105*1mm,  and then cut φ12 bars of stainless steel 304 with the prepared disks. The results are as follows.

 

磨料品種Abrasive Variety

切割時間Cutting time

使用壽命

Service life

燒傷度

Burning degree

 

YF2A

2.1s

45

 

整形棕剛玉

Shaped brown corundum

3.0s

40

30%

 

球磨棕剛玉

Ball milled brown corundum

2.7s

35

28%


對輥棕剛玉

Roller milled brown corundum

2.5s

30

25%


 

 

 

 

 

 

 

 

 

 

 

 

 

 



2)采用YF2A和藍色單晶剛玉分別105*1mm切割片,切割304不銹鋼φ12棒材,對比試驗結果如下:

Use YF2A and blue monocrystal corundum respectively to make Cutting disks in size of φ105*1mm, then cut the φ12 bars of stainless steel 304. The results are as follows.

 

磨料品種

Abrasive Variety

切割時間Cutting time

使用壽命Service life

燒傷度

Burning degree

 

藍色單晶剛玉

Blue single crystal corundum

 

1.9 s

 

32

5%

YF2A

2.1 s

44

5%


  磨削試驗grinding test

鉻剛玉,YF2A兩者都用46#砂制平面磨砂輪,進行磨削45#鋼、40 Cr鋼的對比試驗,結果如下:

46Sand plane grinding wheels used chrome corundum and YF2A, respectively to mill 45steel and 40 Cr steel. The results are as follows.

 

磨料品種

Abrasive Variety

燒傷度Burning degree

 

鉻剛玉

Chrome corundum

燒傷Burned

YF2A

Unburned









The attached figure is the stack of the products.